Abstract

Preparation and characterization of perovskite LaAlO3 nanocrystals

The aim of said study was to obtain nanostructured LaAlO3 through self combustion synthesis using lanthanum nitrate, aluminium nitrate as precursors and glycine as a fuel, without the subsequent heat treatments after synthesis. The temperature variation with respect to a sample with constant molar ratio was investigated. The crystallinity ( phases present and crystallite size: estimated by single-line method ) of the product obtained was determined by X-ray diffraction (XRD) measurement, thermogravimetric analysis(TG-DTA),scanning electron microscope(SEM),and transmission electron microscopy (TEM). The synthesis method facilitated the production of Perovskite LaAlO3 with crystallite size between 40-70 nm.


Author(s): K. A. Khamkar1, S. V. Bangale2, S. R. Bamane2 and V. V. Dhapte1

Abstract | PDF

Share This Article
Awards Nomination 17+ Million Readerbase
Google Scholar citation report
Citations : 5682

Der Chemica Sinica received 5682 citations as per Google Scholar report

Der Chemica Sinica peer review process verified at publons
Abstracted/Indexed in
  • Google Scholar
  • Open J Gate
  • Genamics JournalSeek
  • China National Knowledge Infrastructure (CNKI)
  • Directory of Research Journal Indexing (DRJI)
  • Publons
  • MIAR
  • International Committee of Medical Journal Editors (ICMJE)
  • Serials Union Catalogue (SUNCAT)
  • Geneva Foundation for Medical Education and Research
  • Secret Search Engine Labs
  • Euro Pub
  • CAS (Chemical Abstracting Services)
  • University of Barcelona

View More »

Flyer image
T�rkiye'nin Yeni Nesil Bahis Adresi Matadorbet giris Adresi G�ncellenmistir!