Behavior of dielectric constant and dielectric loss tangent in Cd2+ and Cr3+ substituted magnesium ferrites

Spinel ferrites with general formula CdxMg1-xFe2-yCryO4 (x=0,0.2,0.4, 0.6, 0.8, and 1.00; y=0, 0.05 and 0.10) were prepared by standard ceramic method. Dielectric constant (έ) and dielectric loss tangent (tan δ) were determined in the frequency range 20Hz to 1MHz at room temperature. To study the behavior, έ and tan δ were plotted against frequency. These plots show dispersion at lower frequencies. Such behavior is attributed to the Maxwell-Wagner interfacial polarization. It is also found that Dielectric constant increases with cadmium content while it decreases with chromium content. This is explained on the basis of conduction mechanism, wherein addition of cadmium content increases conduction and decreases with chromium content


Author(s): S. A. Mastia, A. K. Sharmab and P. N. Vasambekar

Abstract | PDF

Share this  Facebook  Twitter  LinkedIn  Google+
Flyer image

Abstracted/Indexed in

  • Chemical Abstracts Service (CAS)
  • Index Copernicus
  • Google Scholar
  • Genamics JournalSeek
  • China National Knowledge Infrastructure (CNKI)
  • CiteFactor
  • Electronic Journals Library
  • Directory of Research Journal Indexing (DRJI)
  • WorldCat
  • Proquest Summons
  • Publons
  • Serials Union Catalogue (SUNCAT)
  • Geneva Foundation for Medical Education and Research
  • Secret Search Engine Labs